| Ferro Chrome |
 |
 |
 |
| HIGH CARBON FERRO CHROME |
| GRADE |
Cr |
Silicon |
Carbon |
Sulphur |
Phos |
Size |
| Standard |
60% Min |
3-4%Max |
6-8% Max |
0.04%Max |
0.015-0.03% Max |
10-150 mm |
| Ferro Manganese |
 |
 |
 |
| HIGH CARBON FERRO MANGANESE
|
| GRADE |
Mn |
Silicon |
Carbon |
Sulphur |
Phos |
Size |
| Standard |
70-75% |
1.5% Max |
6%-8% |
0.05% |
0.40% Max |
10-150 mm |
| Ferro Silicon |
 |
 |
 |
| FERRO SILICON |
| GRADE |
Mn |
Silicon |
Carbon |
Sulphur |
Phos |
Size |
| Standard |
0.50% Max |
70-75% |
0.10% Max |
0.04% Max |
0.06% Max |
10-150 mm |
| Silicon Manganese |
 |
 |
| HIGH CARBON SILICO MANGANESE |
| GRADE |
Mn |
Silicon |
Carbon |
Sulphur |
Phos |
Size |
| I |
65-70% Min |
15%Min |
2%Max |
0.05%Max |
0.35%Max |
10-150 mm |
| II |
60-65% Min |
15% Min |
2% Max |
0.05% Max |
0.35 % Max |
10-150 mm |
| III |
60-65% Min |
14% Min |
2.25% Max |
0.05% Max |
0.35 % Max |
10-150 mm |
| IV |
60-65% Min |
13% Min |
2.5% Max |
0.05% Max |
0.35 % Max |
10-150 mm |
| Noble Alloys |
 |
 |
 |
| FERRO MOLYBDENUM |
FERRO TITANIUM |
FERRO VANADIUM |
| FERRO MOLYBDENUM |
| Mo |
C |
Si |
Cu |
P |
S |
| 60%Min. |
0.1%Max. |
2% Max. |
0.5% Max. |
0.05% Max. |
0.1% Max. |
| FERRO TITANIUM |
| TI |
C |
Si |
Mn |
P |
S |
| 70% Min |
0.2%Max. |
0.3% Max. |
0.02% Max. |
0.02% Max. |
0.02% Max. |
| FERRO VANADIUM |
| V (Min) |
C (Max) |
Al(Max) |
Si (Max) |
P (Max) |
S (Max) |
| 75-85% |
0.20% |
4.0% |
2.0% |
0.10% |
0.10% |
| 75-85% |
0.20% |
1.5% |
1.5% |
0.06% |
0.05% |
| 50% |
0.50% |
1.o% |
2.0% |
0.10% |
0.05% |
|
|
 |